CC0100CRNPO7BN5R6

DATA SHEET SURFACE-MOUNT CERAMIC MULTILAYER CAPACITORS 01005 NP0/X5R/X7R 4 V TO 25 V 0.5 pF to 470 nF Product Specification – May 5, 2017 V.10 RoHS compliant & Halogen Free Product specification Surface-Mount Ceramic Multilayer Capacitors 01005 NP0/X5RX7R 4V to 25V SCOPE ORDERING INFORMATION - GLOBAL PART NUMBER, PHYCOMP This specification describes 01005 NP0/X5R series chip capacitors with lead-free terminations. CTC & 12NC APPLICATIONS  Mobile  Module GLOBAL PART NUMBER (PREFERRED ) 2 11 All part numbers are identified by the series, size, tolerance, TC material, packing style, voltage, process code, termination and capacitance value. YAGEO BRAND ordering code CC XXXX X X XXX X (1) (2) (3) (4) (5) B X XXX (6) (7) (1) SIZE – INCH BASED (METRIC) FEATURES  Supplied in tape on reel  Nickel-barrier end termination  RoHS compliant  Halogen Free compliant 0100(0402) (2) TOLERANCE B = ± 0.1pF C = ± 0.25pF D = ± 0.5pF J = ± 5% K = ± 10% M = ± 20% (3) PACKING STYLE R = Paper/PE taping reel; Reel 7 inch (4) TC MATERIAL NPO X5R X7R (5) RATED VOLTAGE 4= 4 V 5 = 6.3 V 6 = 10 V 7 = 16 V 8 = 25 V (6) PROCESS N = NP0 B = Class 2 MLCC (7) CAPACITANCE VALUE 2 significant digits+number of zeros The 3rd digit signifies the multiplying factor, and letter R is decimal point Example: 121 = 12 x 101 = 120 pF www.yageo.com May. 5, 2017 V.10 Product specification Surface-Mount Ceramic Multilayer Capacitors 01005 NP0/X5RX7R 4V to 25V 3 11 CONSTRUCTION The capacitor consists of a rectangular block of ceramic dielectric in which a number of interleaved metal electrodes are contained. This structure gives rise to a high capacitance per unit volume. The inner electrodes are connected to the two end terminations and finally covered with a layer of plated tin (NiSn). The terminations are lead-free. A cross section of the structure is shown in Fig.1. Fig. 1 Surface mounted multilayer ceramic capacitor construction DIMENSION Table 1 For outlines see fig. 2 TYPE L1 (mm) W (mm) 01005 0.4 ± 0.02 0.2 ± 0.02 OUTLINES T (mm) 0.2 ± 0.02 L2 / L3 (mm) L4 (mm) min. max. min. 0.07 0.14 0.13 For dimension see Table 1 Fig. 2 Surface mounted multilayer ceramic capacitor dimension www.yageo.com May. 5, 2017 V.10 Product specification Surface-Mount Ceramic Multilayer Capacitors CAPACITANCE RANGE & THICKNESS Table 2 01005 Sizes NP0 CAP. CAP. 16 V / 25 V 01005 X5R NP0/X5RX7R 6.3V 10V 4 11 X7R CAP. 4V 4V to 25V 6.3V / 10V 16V 0.5 pF 0.2±0.02 100 pF 0.2±0.02 0.2±0.02 0.2±0.02 100 pF 0.2±0.02 0.2±0.02 0.6 pF 0.2±0.02 150 pF 0.2±0.02 0.2±0.02 0.2±0.02 150 pF 0.2±0.02 0.2±0.02 0.7 pF 0.2±0.02 220 pF 0.2±0.02 0.2±0.02 0.2±0.02 220 pF 0.2±0.02 0.2±0.02 0.75 pF 0.2±0.02 330 pF 0.2±0.02 0.2±0.02 0.2±0.02 330 pF 0.2±0.02 0.2±0.02 0.8 pF 0.2±0.02 470 pF 0.2±0.02 0.2±0.02 0.2±0.02 470 pF 0.2±0.02 0.2±0.02 0.9 pF 0.2±0.02 680 pF 0.2±0.02 0.2±0.02 0.2±0.02 680 pF 0.2±0.02 0.2±0.02 1.0 pF 0.2±0.02 1 000 pF 0.2±0.02 0.2±0.02 0.2±0.02 1 000 pF 0.2±0.02 0.2±0.02 1.2 pF 0.2±0.02 2.2 nF 0.2±0.02 0.2±0.02 0.2±0.02 2.2 nF 1.5 pF 0.2±0.02 4.7 nF 0.2±0.02 0.2±0.02 0.2±0.02 4.7 nF 1.8 pF 0.2±0.02 10 nF 0.2±0.02 0.2±0.02 0.2±0.02 10 nF 2.2 pF 0.2±0.02 22nF 0.2±0.02 0.2±0.02 22nF 2.7 pF 0.2±0.02 47 nF 0.2±0.02 0.2±0.02 47 nF 3.3 pF 0.2±0.02 100 nF 0.2±0.02 0.2±0.02 3.9 pF 0.2±0.02 220 nF 0.2±0.02 0.2±0.02 220 nF 4.7 pF 0.2±0.02 470 nF 0.2±0.02 0.2±0.02 Tape width 5.6 pF 0.2±0.02 Tape width 6.8 pF 0.2±0.02 8.2 pF 0.2±0.02 10 pF 0.2±0.02 12 pF 0.2±0.02 15 pF 0.2±0.02 18 pF 0.2±0.02 22 pF 0.2±0.02 27 pF 0.2±0.02 33 pF 0.2±0.02 39 pF 0.2±0.02 47 pF 0.2±0.02 56 pF 0.2±0.02 68 pF 0.2±0.02 82 pF 0.2±0.02 100 pF 0.2±0.02 Tape width 0.2±0.02 100 nF 8 mm 8 mm 8 mm www.yageo.com May. 5, 2017 V.10 Product specification Surface-Mount Ceramic Multilayer Capacitors 01005 NP0/X5RX7R 5 11 4V to 25V THICKNESS CLASSES AND PACKING QUANTITY Table 3 Ø 180 MM / 7 INCH Ø 330 MM / 13 INCH SIZE CODE THICKNESS CLASSIFICATION TAPE WIDTH QUANTITY PER REEL Paper/PE Blister Paper/ Blister QUANTITY PER BULK CASE 01005 0.2 ± 0.02 mm 8 mm 20,000 --- --- --- --- ELECTRICAL CHARACTERISTICS NP0/X5R DIELECTRIC CAPACITORS; NISN TERMINATIONS Unless otherwise specified, all test and measurements shall be made under standard atmospheric conditions for testing as given in 5.3 of IEC 60068-1: - Temperature: 15 °C to 35 °C Relative humidity: 25% to 75% Air pressure: 86 kPa to 106 kPa Before the measurements are made, the capacitor shall be stored at the measuring temperature for a time sufficient to allow the entire capacitor to reach this temperature. The period as prescribed for recovery at the end of a test is normally sufficient for this purpose. Table 4 VALUE DESCRIPTION Capacitance range 0.5 pF to 470 nF Capacitance tolerance NP0 C< 10 pF ± 0.1pF, ± 0.25pF, ± 0.5pF C ≥ 10 pF ± 5%, ± 10% X5R / X7R ± 10%, ± 20% Dissipation factor (D.F.) NP0 C < 30 pF ≤ 1 / ( 400 + 20C ) C ≥ 30 pF ≤ 0.1 % X5R / X7R Insulation resistance after 1 minute at Ur (DC) ≤ 10 % Rins ≥ 10 GΩ or Rins × C ≥ 500Ω · F whichever is less X5R/X7R > 10nF: Rins x C ≥ 50Ω· F Maximum capacitance change as a function of temperature (temperature characteristic/coefficient): NP0 X5R / X7R ± 30 ppm/°C ± 15% Operating temperature range: NP0 –55 °C to +125 °C X5R –55 °C to +85 °C X7R –55 °C to +125 °C www.yageo.com May. 5, 2017 V.10 Product specification Surface-Mount Ceramic Multilayer Capacitors 01005 NP0/X5RX7R 4V to 25V 6 11 SOLDERING RECOMMENDATION Table 5 SOLDERING METHOD Reflow SIZE 01005 Reflow only Reflow/Wave --- TESTS AND REQUIREMENTS Table 6 Test procedures and requirements TEST TEST METHOD PROCEDURE REQUIREMENTS Mounting IEC 60384- 4.3 21/22 The capacitors may be mounted on printed-circuit boards or ceramic substrates No visible damage Visual Inspection and Dimension Check 4.4 Any applicable method using × 10 magnification In accordance with specification Capacitance 4.5.1 Class 1: f = 1 MHz for C ≤ 1 nF, measuring at voltage 1 Vrms at 20 °C f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 °C Within specified tolerance Class 2: C ≤ 1 nF f = 1 KHz, measuring at voltage 1 Vrms at 20 °C Dissipation Factor (D.F.) 4.5.2 C > 1 nF f = 1 KHz, rated voltage ≤ 6.3 V, measuring at voltage 0.5 Vrms at 20 °C f = 1 KHz, rated voltage > 10 V, measuring at voltage 1 Vrms at 20 °C Class 1: f = 1 MHz for C ≤ 1 nF , measuring at voltage 1 Vrms at 20 °C f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 °C In accordance with specification Class 2: C ≤ 1 nF f = 1 KHz, measuring at voltage 1 Vrms at 20 °C C > 1 nF f = 1 KHz, rated voltage ≤ 6.3 V, measuring at voltage 0.5 Vrms at 20 °C f = 1 KHz, rated voltage > 10 V, measuring at voltage 1 Vrms at 20 °C Insulation Resistance 4.5.3 At Ur (DC) for 1 minute In accordance with specification www.yageo.com May. 5, 2017 V.10 Product specification Surface-Mount Ceramic Multilayer Capacitors TEST TEST METHOD 4.6 Temperature coefficient NP0/X5RX7R 01005 PROCEDURE REQUIREMENTS Capacitance shall be measured by the steps shown in the following table. ∆C/C The capacitance change should be measured after 5 min at each specified temperature stage. Step Temperature(℃) a 25± 2 b Lower temperature± 3℃ c 25± 2 d Upper Temperature± 2℃ e 25± 2 (1) Class I 4V to 25V 7 11 Class1 (NP0): ± 30ppm Class 2: (X7R/X5R): ± 15% In case of applying voltage, the capacitance change should be measured after 1 more min. with applying voltage in equilibration of each temp. stage. CC0100MRX5R4(5)BB104(224): 0.2V± 0.1Vrms Temperature Coefficient shall be calculated from the formula as below C2 - C1 106 [ppm/℃] Temp, Coefficient = C1 xΔT C1: Capacitance at step c C2: Capacitance at 125℃ ∆T: 100℃(=125℃-25℃) Measuring Voltage: 0.5 to 5 Vrms (2) Class II Capacitance Change shall be calculated from the formula as below ∆C = C2 - C1 x 100% C1 C1: Capacitance at step c C2: Capacitance at step b or d Adhesion Bending Strength IEC 6038421/22 4.7 A force applied for 10 seconds to the line joining the terminations and in a plane parallel to the substrate Force size 01005 : 1N 4.8 Mounting in accordance with IEC 60384-22 paragraph 4.3 No visible damage Conditions: bending 1 mm at a rate of 1 mm/s, radius jig 5 mm ∆C/C Class 1 (NP0): within ± 1% or 0.5 pF, whichever is greater Class2 (X5R/X7R): ± 10% www.yageo.com May. 5, 2017 V.10 8 Product specification Surface-Mount Ceramic Multilayer Capacitors TEST TEST METHOD 4.9 Resistance to Soldering Heat 01005 NP0/X5RX7R 4V to 25V 11 PROCEDURE REQUIREMENTS Precondition: 150 +0/–10 °C for 1 hour, then keep for 24 ± 1 hours at room temperature Dissolution of the end face plating shall not exceed 25% of the length of the edge concerned Preheating: 120 °C to 150 °C for 1 minute and 170 °C to 200 °C for 1 minute. ∆C/C Class 1 (NP0): within ± 0.5% or 0.5 pF, whichever is greater Solder bath temperature: 260 ± 5 °C Dipping time: 10 ± 0.5 seconds Recovery time: 24 ± 2 hours Class2 (X5R/X7R): ± 10% D.F. within initial specified value Rins within initial specified value 4.10 Solderability Preheated the temperature of 80 °C to 140 °C and maintained for 30 seconds to 60 seconds. The solder should cover over 95% of the critical area of each termination Test conditions for leadfree containing solder alloy Temperature: 245 ± 5 °C Dipping time: 3 ± 0.3 seconds Depth of immersion: 10 mm Rapid Change of Temperature IEC 6038421/22 4.11 Preconditioning; 150 +0/–10 °C for 1 hour, then keep for 24 ± 1 hours at room temperature 5 cycles with following detail: 30 minutes at lower category temperature 30 minutes at upper category temperature Recovery time 24 ± 2 hours No visual damage ∆C/C Class 1 (NP0): within ± 2.5% or 0.25 pF, whichever is greater Class2 (X5R/X7R): ± 15% D.F. meet initial specified value Rins meet initial specified value www.yageo.com May. 5, 2017 V.10 Product specification Surface-Mount Ceramic Multilayer Capacitors 01005 NP0/X5RX7R 4V to 25V TEST TEST METHOD PROCEDURE REQUIREMENTS Damp Heat with Ur load 1. Preconditioning, class 2 only: No visual damage after recovery 4.13 150 +0/-10 °C /1 hour, then keep for 24 ± 1 hour at room temp 2. Initial measure: Spec: refer initial spec C, D, IR 3. Damp heat test: 500 ± 12 hours at 40 ± 2 °C; 90 to 95% R.H; 1.0 Ur applied. 4. Recovery: Class 1: 6 to 24 hours Class 2: 24 ± 2 hours 5. Final measure: C, D, IR P.S. If the capacitance value is less than the minimum value permitted, then after the other measurements have been made the capacitor shall be precondition according to “IEC 60384 4.1” and then the requirement shall be met. 9 11 Class 1 (NP0): ∆C/C within ± 7.5% or 0.75 pF, whichever is greater D.F. ≤ 2 x specified value I.R. ≥ 2,500 MΩ or Rins x Cr ≥ 25Ω· F whichever is less Class2 (X5R/X7R): C ≤ 1nF ∆C/C ± 15% D.F. ≤ 10% I.R. ≥ 500 MΩ 10nF ≥ C > 1nF ∆C/C ± 20% D.F. ≤ 10% I.R. ≥ 500 MΩ C > 10nF ∆C/C ± 25% D.F. ≤ 20% I.R. Rins x Cr ≥ 5Ω· F www.yageo.com May. 5, 2017 V.10 Product specification Surface-Mount Ceramic Multilayer Capacitors 01005 NP0/X5RX7R TEST TEST METHOD PROCEDURE REQUIREMENTS Endurance IEC 6038421/22 1. Preconditioning, class 2 only: No visual damage 4.14 150 +0/-10 °C /1 hour, then keep for 24 ± 1 hour at room temp 2. Initial measure: Spec: refer initial spec C, D, IR 3. Endurance test: Temperature: NP0: 125 °C Specified stress voltage applied for 1,000 hours: Applied 2.0 x Ur for general product Temperature: X5R: 85°C, X7R: 125°C Specified stress voltage applied for 1,000 hours: Applied 1.5 x Ur for general product 4. Recovery time: 24 ± 2 hours 5. Final measure: C, D, IR P.S. If the capacitance value is less than the minimum value permitted, then after the other measurements have been made the capacitor shall be precondition according to “IEC 60384 4.1” and then the requirement shall be met. 4V to 25V 10 11 Class 1 (NP0): ∆C/C within ± 3% or 0.3 pF, whichever is greater D.F. ≤ 2 x specified value I.R. ≥ 4,000 MΩ or Rins x Cr ≥ 40Ω· F whichever is less Class2 (X5R/X7R): C ≤ 1nF ∆C/C ± 15% D.F. ≤ 10% I.R. ≥ 1GΩ 10nF ≥ C >1nF ∆C/C ± 15% D.F. ≤ 10% I.R. ≥ 1GΩ C >10nF ∆C/C ± 25% D.F. ≤ 20% I.R. Rins x Cr ≥ 10Ω· F Voltage Proof IEC 60384-1 4.5.4 Specified stress voltage applied for 1~5 seconds No breakdown or flashover Ur ≤ 100 V: series applied 2.5 Ur Charge/Discharge current is less than 50 mA www.yageo.com May. 5, 2017 V.10 Product specification Surface-Mount Ceramic Multilayer Capacitors 01005 NP0/X5RX7R 4V to 25V 11 11 REVISION HISTORY REVISION DATE CHANGE NOTIFICATION DESCRIPTION Version 10 May 5, 2017 - - Rated voltage of NPO series extend to 25 V Version 9 Jan. 17, 2017 - - Test condition updated Version 8 Jan. 12, 2016 - - Capacitance range & thickness update Version 7 Oct. 31, 2015 - - Capacitance range & thickness update Version 6 Jun. 29, 2015 - - Test procedures and requirements Version 5 Jun. 06, 2013 - - Test procedures and requirements Version 4 Mar. 27, 2013 - - Change Tolerance Version 3 Jan. 15, 2013 - - Change Range Version 2 Oct. 23, 2012 - - Change Range Version 1 July 03, 2012 - - Change Range Version 0 Apr 16, 2012 - - New - Add X5R, 470nF, 4V to 6.3V and 100nF, 10V www.yageo.com May. 5, 2017 V.10